Post-Treatment Agent for Sealing AST-1

Classification:

Auxiliaries for Anodizing

Tag:

online message

Product Details

Name Type

Oxidation Additive

Model/Specification

AST-1

SpecialProperty

Sealing AgentPost-Treatment Agent AST-1is atreatment agent used for soaking workpieces after sealing.

After treatmentenhances the product's UV resistance,acid and alkali resistance.
It is suitable for treatment after nickel-containing sealing,andalso suitable for treatment after nickel-free sealing.After treatment, the product does not change the surface effect.
The occurrence of flow marks is less than that of similar products.
The working solution has a long usage cycle and is not prone to whitening.
Appearance


Light yellow transparent liquid Heavier	Usage Conditions
Recommended Concentration	1.08


	per liter Temperature	°C Value
Time Minutes	100Packaging/and Storage-140Packaging/and Storage	110 Packaging/and Storage
Kilograms Minutes	70-90Barrel, liquid form, stored in	80Barrel, liquid form, stored in
pHa cool, dry warehouse, avoid	10.5-11.2	11.0
direct sunlight, high temperatures, and must be sealed after use. Precautions	10-30It is recommended to wear protective equipment when using this product	20It is recommended to wear protective equipment when using this product

including safety glovesmasks and goggles

25Control Methods/(1)The concentration of the post-treatment agent after sealing will not change significantly during normal use, basically onlycarried out with the workpiece, so there is generally no need to adjust the concentration during use, just add the same concentration solution when the liquid level drops.If it drops below

then add

the original liquid to adjustalso suitable for treatment after nickel-free sealing.the value.also suitable for treatment after nickel-free sealing.(2).

After the workpiece is taken out from the post-treatment agent

, it should be washed with water as soon as possible, otherwise the surface mayleave marks.AST-1(3)

After washing, it is recommended to dry at

above °C for minutes to enhance the effect.pH降低至10.5以下，则补加

原液调整pH值。

(2)工件从封孔后处理剂AST-1取出后，需尽快用水清洗，否则表面可能

会出现留痕。

(3)清洗完毕后，建议在80℃以上烘干20分钟以加强效果